Immediate bond strength (MPa) · Dental adhesives/resin composite bonded to dentin (in vitro), sound or caries-affected
Prior SDF application significantly reduces the immediate bond strength of adhesives to dentin overall (MD 7.12 MPa favoring untreated dentin, 95% CI 1.38 to 12.85; ungraded), with very high heterogeneity (I2=98%).
1 finding from 1 review
Immediate bond strength (MPa) · Glass-ionomer cement bonded to dentin (in vitro), sound or caries-affected
Prior SDF application does not influence the immediate bond strength of glass-ionomer cement to dentin (MD -0.11 MPa, 95% CI -0.54 to 0.31; ungraded).
1 finding from 1 review
Immediate (24 h) resin-dentin bond strength (MPa) · Artificial caries-affected dentin (ACAD) in extracted permanent human teeth (in vitro)
Only one in vitro study assessed a Self-Etch adhesive with the biological ACAD protocol; it was insufficient for network meta-analysis, so no pooled effect estimate is available (ungraded).
1 finding from 1 review
Immediate bond strength (MPa) · Glass-ionomer cement bonded to caries-affected dentin (in vitro)
SDF pretreatment without a rinsing step does not affect glass-ionomer cement bond strength to caries-affected dentin (MD 0.26 MPa, 95% CI -0.30 to 0.82; ungraded).
1 finding from 1 review
Immediate bond strength (MPa) · Dental adhesives bonded to sound dentin (in vitro)
Prior SDF without a rinsing step significantly reduces adhesive bond strength to sound dentin (MD 17.52 MPa favoring untreated dentin, 95% CI 5.81 to 29.22; ungraded).
1 finding from 1 review
Immediate bond strength (MPa) · Glass-ionomer cement bonded to sound dentin (in vitro)
SDF pretreatment with a rinsing step does not affect glass-ionomer cement bond strength to sound dentin (MD -1.11 MPa, 95% CI -3.47 to 1.25; ungraded).
1 finding from 1 review
Immediate bond strength (MPa) · Glass-ionomer cement bonded to caries-affected dentin (in vitro)
SDF pretreatment with a rinsing step does not affect glass-ionomer cement bond strength to caries-affected dentin (MD -0.36 MPa, 95% CI -1.07 to 0.35; ungraded).
1 finding from 1 review
Immediate bond strength (MPa) · Glass-ionomer cement bonded to sound dentin (in vitro)
SDF pretreatment without a rinsing step does not affect glass-ionomer cement bond strength to sound dentin (MD 0.26 MPa, 95% CI -0.20 to 0.73; ungraded).
1 finding from 1 review
Immediate bond strength (MPa) · Dental adhesives bonded to sound dentin (in vitro)
A rinsing step after SDF eliminates the negative effect on adhesive bond strength to sound dentin (MD 7.11 MPa, 95% CI -0.57 to 14.79, non-significant; ungraded).
1 finding from 1 review
Immediate bond strength (MPa) · Dental adhesives bonded to caries-affected dentin (in vitro)
Prior SDF followed by a rinsing step significantly increases adhesive bond strength to caries-affected dentin (MD -4.79 MPa favoring SDF, 95% CI -9.19 to -0.40; ungraded).
1 finding from 1 review
Immediate bond strength (MPa) · Dental adhesives bonded to caries-affected dentin (in vitro)
Only one study assessed SDF without a rinsing step on adhesive bonding to caries-affected dentin (Kucukyilmaz 2016, which reported impaired bond strength); no meta-analysis was possible, so no pooled estimate is available.
1 finding from 1 review