Prior SDF application without a rinsing step vs No prior SDF application (untreated dentin control)

Immediate bond strength (MPa) · Dental adhesives bonded to sound dentin (in vitro)

Prior SDF without a rinsing step significantly reduces adhesive bond strength to sound dentin (MD 17.52 MPa favoring untreated dentin, 95% CI 5.81 to 29.22; ungraded).

1 finding from 1 review

Prior SDF application without a rinsing step vs No prior SDF application (untreated dentin control)

Immediate bond strength (MPa) · Dental adhesives bonded to caries-affected dentin (in vitro)

Only one study assessed SDF without a rinsing step on adhesive bonding to caries-affected dentin (Kucukyilmaz 2016, which reported impaired bond strength); no meta-analysis was possible, so no pooled estimate is available.

1 finding from 1 review

Prior application of silver diamine fluoride (SDF), with or without a rinsing step vs No prior SDF application (untreated dentin control)

Immediate bond strength (MPa) · Dental adhesives/resin composite bonded to dentin (in vitro), sound or caries-affected

Prior SDF application significantly reduces the immediate bond strength of adhesives to dentin overall (MD 7.12 MPa favoring untreated dentin, 95% CI 1.38 to 12.85; ungraded), with very high heterogeneity (I2=98%).

1 finding from 1 review

Prior SDF application without a rinsing step vs No prior SDF application (untreated dentin control)

Immediate bond strength (MPa) · Glass-ionomer cement bonded to caries-affected dentin (in vitro)

SDF pretreatment without a rinsing step does not affect glass-ionomer cement bond strength to caries-affected dentin (MD 0.26 MPa, 95% CI -0.30 to 0.82; ungraded).

1 finding from 1 review

Prior SDF application without a rinsing step vs No prior SDF application (untreated dentin control)

Immediate bond strength (MPa) · Glass-ionomer cement bonded to sound dentin (in vitro)

SDF pretreatment without a rinsing step does not affect glass-ionomer cement bond strength to sound dentin (MD 0.26 MPa, 95% CI -0.20 to 0.73; ungraded).

1 finding from 1 review

Prior application of silver diamine fluoride (SDF), with or without a rinsing step vs No prior SDF application (untreated dentin control)

Immediate bond strength (MPa) · Glass-ionomer cement bonded to dentin (in vitro), sound or caries-affected

Prior SDF application does not influence the immediate bond strength of glass-ionomer cement to dentin (MD -0.11 MPa, 95% CI -0.54 to 0.31; ungraded).

1 finding from 1 review